Superionic Conduction over a Wide Temperature Range in a Metal-Organic Framework Impregnated with Ionic Liquids.

Most molecules in confined spaces show markedly different behaviors from those in the bulk. Large pores are composed of two regions: an interface region in which liquids interact with the pore surface, and a core region in which liquids behave as bulk. The realization of a highly mobile ionic liquid (IL) in a mesoporous metal-organic framework (MOF) is now reported. The hybrid shows a high room-temperature conductivity (4.4×10-3  S cm-1 ) and low activation energy (0.20 eV); both not only are among the best values reported for IL-incorporated MOFs but also are classified as a superionic conductor. The conductivity reaches over 10-2  S cm-1 above 343 K and follows the Vogel-Fulcher-Tammann equation up to ca. 400 K. In particular, the hybrid is advantageous at low temperatures (<263 K), where the ionic conduction is superior to that of bulk IL, making it useful as solid-state electrolytes for electrochemical devices operating over a wide temperature range.

Low temperature ionic conductor: ionic liquid incorporated within a metal-organic framework.

Ionic liquids (ILs) show promise as safe electrolytes for electrochemical devices. However, the conductivity of ILs decreases markedly at low temperatures because of strong interactions arising between the component ions. Metal-organic frameworks (MOFs) are appropriate microporous host materials that can control the dynamics of ILs via the nanosizing of ILs and tunable interactions of MOFs with the guest ILs. Here, for the first time, we report on the ionic conductivity of an IL incorporated within a MOF. The system studied consisted of EMI-TFSA (1-ethyl-3-methylimidazolium bis(trifluoromethylsulfonyl)amide) and ZIF-8 (Zn(MeIM)2, H(MeIM) = 2-methylimidazole) as the IL and the MOF, respectively. While the ionic conductivity of bulk EMI-TFSA showed a sharp decrease arising from freezing, the EMI-TFSA@ZIF-8 showed no marked decrease because there was no phase transition. The ionic conductivity of EMI-TFSA@ZIF-8 was higher than that of bulk EMI-TFSA below 250 K. This result points towards a novel method by which to design electrolytes for electrochemical devices such as batteries that can operate at low temperatures.

Introduction of an ionic liquid into the micropores of a metal-organic framework and its anomalous phase behavior.

Controlling the dynamics of ionic liquids (ILs) is a significant issue for widespread use. Metal-organic frameworks (MOFs) are ideal host materials for ILs because of their small micropores and tunable host-guest interactions. Herein, we demonstrate the first example of an IL incorporated within the micropores of a MOF. The system studied consisted of EMI-TFSA (1-ethyl-3-methylimidazolium bis(trifluoromethylsulfonyl)amide) and ZIF-8 (composed of Zn(MeIM)2 ; H(MeIM)=2-methylimidazole) as the IL and MOF, respectively. Construction of the EMI-TFSA in ZIF-8 was confirmed by X-ray powder diffraction, nitrogen gas adsorption, and infrared absorption spectroscopy. Differential scanning calorimetry and solid-state NMR measurements showed that the EMI-TFSA inside the micropores demonstrated no freezing transition down to 123 K, whereas bulk EMI-TFSA froze at 231 K. Such anomalous phase behavior originates from the nanosize effect of the MOF on the IL. This result provides a novel strategy for stabilizing the liquid phase of the ILs down to a lower temperature region.